SynTherm® – Insulating Materials SynTherm® YT510 DDP

SynTherm® YT510 DDP is a synthetic electro-insulation paper constructed of a calandered, aromatic polyamide fibride flock composition. Both sides of the paper are printed with a B-stage Epoxy resin in a diamond dotted pattern.

The base material SynTherm® YT510 is a Class H (180 °C) insulating material. Temperatures below 200 °C only slightly influence its electrical properties. The good mechanical properties can be extrapolated to significantly higher temperatures. SynTherm® YT510 is also suitable for us at temperatures to -190 °C due to its polymer-structure. It has a high short-term dielectric strength. SynTherm® YT510 is compatible with all classes of common resins, varnishes, adhesives as well as transformer liquids, lubricants, and cooling agents. Common solvents may lead to slight reversible moisture expansion. SynTherm® YT510 has low flammability (UL 94V-0) and very high resistance to beta and gamma radiation.

Download datasheet

Application

SynTherm® YT510 DDP is used as layer insulation in transformers.

Standards

  • Insulating material class F (155 °C). Base material class H (180 °C)
  • The base material is UL listed (RTI mech. + electr. 210 °C)

Delivery forms

Film thickness in μm:
50, 80, 130, 180, 250, 300, 380, 510, 760

SYNTHERM® YT510 DDP is available:

  • in tapes: depending on material thickness on request beginning at 6mm (thin material)
  • in rolls: 1000 mm

Feathering:

  • depth approx. 1 - 12 mm, distance approx. 1 - 10 mm
  • 10 mm up to 240 mm width, thickness on request

Base

Calandered, aromatic polyamide fibride flock composition with diamond dotted B-stage resin on both sides.

Technical data

Mechanical
Property Unit of measure Test standard
Nominal thickness μm 80 130 180 250 300 380 510 760
Typical thickness µm 78 130 180 245 290 365 515 755 GB/T451.3-2002
Specific weight g/m² 63 116 175 249 309 390 510 690 GB/T451.2-2002
Tensile strength longitudinal N/cm 66 140 225 255 320 380 500 650 GB/T12914-2008
Tensile strength transversal N/cm 29 56 105 165 200 260 345 450 GB/T12914-2008
Elongation at break longitudinal % 8.5 10 11 13.5 16 13 13 13 GB/T12914-2008
Elongation at break transversal % 9 11.5 12.5 14.5 15.5 12 13 12 GB/T12914-2008
Shrinkage at 300 °C longitudinal % 3.5 3.0 3.0 3.0 3.0 3.0 3.0 3.0 IEC60819-2:2002
Shrinkage at 300 °C transversal % 3.0 2.5 2.5 2.5 2.5 2.5 2.0 2.0 IEC60819-2:2002
Elmendorf tear strength longitudinal N 1.0 2.0 3.5 5.0 6.5 10.0 13 - GB/T455-2002
Elmendorf tear strength transversal N 1.7 3.3 4.8 6.0 8 13.5 16 - GB/T455-2002
Properties of B-stage resin
Property Unit of measure
Thickness increase (one side) µm 10±15 %
Basic weight increase (both sides) g/m² 5±10 %
Curing conditions h 1 3 10 20 30
Curing conditions °C 130 120 110 100 90
Shelf life 6 months after production
Electrical
Property Unit of measure Test standard
Nominal thickness μm 50 80 130 180 250 300 380 510 760
Field intensity kV/mm 13 14 18 20 22 23 20 18 19 GB/T1408.1-2006
Dielectric constant (50 Hz) 1.5 1.5 2.1 2.4 2.5 2.7 3.0 3.1 3.2 GB/T1409-2006