SynTherm® – Insulating Materials SynTherm® YT511 (metastar® YT511)
SynTherm® YT511 is a synthetic electrical insulating paper consisting of a non-calendered, aromatic polyamide fibride flock composition.
SynTherm® YT511 is a Class H (180 °C) insulating materials. Temperatures of up to 200 °C only slightly influence the electrical properties. The good mechanical properties can be extrapolated to significantly higher temperatures. Due to the polymer structure SynTherm® YT511 can also be used a low temperature of up to -190 °C. It has a very high short-term dielectric strength.
SynTherm® YT511 is compatible with all common classes of resins, varnishes, adhesives and transformer liquids, lubricants and cooling agents. Commonly used solvents may lead to minor, reversible expansion. SynTherm® YT511 paper is of low flammability (UL 94V-0) and very high resistance to beta and gamma radiation
Application
High-quality SynTherm® YT511 is used as electrical insulating material in almost any known application. Used in AC and DC motors, large generators, liquid-immersed and dry transformer, and chokes, even when exposed to beta and gamma radiation.
Standards
- Insulating material Class H (180 °C)
- UL listed (RTI mech. + electr. 210 °C)
- UL file no. E358562
Delivery forms
Film thickness in μm:
130, 180, 250, 380, 580
SynTherm® YT511 is available:
- tapes: depending on material thickness on request
Beginning at 6mm (thin materials)
- rolls: 1030 mm
Feathering:
- depth approx. 1 - 12 mm, distance approx. 1 - 10 mm
- 10 mm to 240 mm width, material thickness on request
Base
Non-calendered, aromatic polyamide flock composition
Technical data
| Property | Unit of measure | Test standard | |||||
|---|---|---|---|---|---|---|---|
| Nominal thickness | µm | 130 | 180 | 250 | 380 | 580 | |
| Typical thickness | µm | 130 | 170 | 250 | 390 | 570 | GB/T451.3-2002 |
| Specific weight | g/m² | 42 | 64 | 82 | 155 | 200 | GB/T451.2-2002 |
| Density | g/cm³ | 0.31 | 0.37 | 0.32 | 0.39 | 0.35 | |
| Tensile strength longitudinal | N/cm | 25 | 40 | 60 | 145 | 170 | GB/T12914-2008 |
| Tensile strength transversal | N/cm | 13 | 21 | 32 | 68 | 85 | GB/T12914-2008 |
| Elongation at break longitudinal | % | 3.3 | 3.7 | 4.5 | 5.5 | 6.0 | GB/T12914-2008 |
| Elongation at break transversal | % | 4.5 | 5.0 | 5.5 | 6.5 | 7.0 | GB/T12914-2008 |
| Shrinkage at 240 °C longitudinal | % | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | IEC60819-2:2002 |
| Shrinkage at 240 °C transversal | % | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | IEC60819-2:2002 |
| Elmendorf tear strength longitudinal | N | 1.2 | 1.8 | 2.0 | 4.5 | 8.5 | GB/T455-2002 |
| Elmendorf tear strength transversal | N | 1.8 | 3.0 | 3.5 | 7.0 | 9.0 | GB/T455-2002 |
| Property | Unit of measure | Test standard | |||||
|---|---|---|---|---|---|---|---|
| Nominal thickness | μm | 130 | 180 | 250 | 380 | 580 | |
| Field intensity | kV/mm | 9 | 9 | 8 | 8 | 7 | GB/T1408.1-2006 |
| Dielectric constant at 60 Hz | 1.3 | 1.3 | 1.3 | 1.4 | 1.4 | GB/T1409-2006 |