Winding wire SHTherm® 210 Flat

  • Enamelled flat copper wire, thermoresistant
  • Polyesterimide overcoated with
  • polyamide-imide enamel
  • Class 200/220

SHTherm® 210 Flat is a highly thermoresistant rectangular enamelled copper wire of heat performance class N with a wide range of excellent quality features. Its insulation film consists of 2 different coatings on top of one another. These ensure a very good permanent thermal and overload resistance, excellent resistance against mechanical stress, as well as an excellent resistance to chemical attacks of commercial washing and cleaning agents, impregnating varnishes and resins, sealing compounds, thinners, solvents and refrigerants, oils as well as their vapours. This range of excellent features make SHTherm® 210 Flat an all-round wire meeting the requirements of all applications with above average requirements to processing and operational features or operational safety in electrical systems.
The consistent further developments carried out by our R&D team allow this excellent “all-round” wire to be optimised to take into account specific customer requirements (e.g. improved adhesion after ageing, workability, electrical characteristics).

Download datasheet

Application

E-mobility, electric motors, generators, transformers, hybrid constructions

Standards

IEC / DIN EN 60317-29
NEMA MW 36-C/ MW 38-C
UL approved

Delivery forms

Grade 1: on request
Grade 2:
width: 2.000 - 20.000 mm
thickness: 0.800 - 5.000 mm

Technical data

Typical properties of enamelled flat copper wire 5.60 x 3.55 mm, with insulation film grade 2

Mechanical
Property Unit of measure Set value Actual value
Bare wire width mm as set value
Width with varnish mm 5.67 - 5.82 as set value
Bare wire thickness mm 3.500-3.600 as set value
Thickness with varnish mm 3.62 - 3.77 as set value
Varnish increase μm 120 - 170 as set value
Elongation and adhesion mandrel diameter
Elongation and adhesion (no cracks in varnish after winding) - bend over width 4 x width 3 x width
Elongation and adhesion (no cracks in varnish after winding) - bend over thickness 4 x thickness 3 x thickness
Elongation and adhesion (no cracks in varnish after winding) - elongation 15 % with cracks < 1 x width 32 % without cracks
Pencil hardness of varnish H 4H - 5H
Elongation at break % ≥ 32 ≥ 38
Bare wire width mm 5.550-5.650

(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used.
Thermal
Property Unit of measure Set value Actual value
Temperature index °C 200/220 210/220
Heat shock at 220 °C (no cracks in varnish coat after winding) mandrel diameter: 6 x thickness mandrel diameter: 4 x thickness
Solderability no no

(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used.
Electrical
Property Unit of measure Set value Actual value
Dielectric strength RT kV ≥ 2.0 (ball pit) ≥ 3 (ball pit)
High voltage discontiniuties 750V / ≤ 7 on 100 m
Electrical conductivity of Cu conductor MS/m 58 - 59 ≥ 58.5

(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used.
Chemical
Property Set value Actual value
Pencil hardness (storage in standard solvent ½ h / 60 °C) min. H 3H - 5H
Pencil hardness (storage in alcohol ½ h / 60 °C) min. H 3H - 5H
Resistance to commercial impregnants^(1) / yes
Resistance to commercial refrigerants^(1) / yes
Resistance to dry transformer oils^(1) / yes
Resistance to hydraulic oils^(1) / yes

(1) Due to the variety of individual applications we cannot make any generally binding commitments regarding the compatibility. We recommend testing compatibility with the materials being used.